Härtung von Stahlspitzen von Handstempeln

Hardening the end of steel hand-held marking stamps


Objective: To harden various size ends of hand held marking stamps. The area to be hardened is 3/4” (19mm) up the shank.


Equipment:
  • Ambrell 30 kW induction heating system, equipped with a remote workhead containing eight 1.0μF capacitors for a total of 2.0μF;
  • An induction heating coil designed and developed specifically for this application.

Material: Steel stamps 1/4” (6.3mm), 3/8” (9.5mm), 1/2” (12.7mm) and 5/8” (15.8mm) square


Temperature: 1550 ºF (843 ºC)



Frequency: 99 kHz


Process:

A two turn channel coil is used to cover the range of steel stamps being heated. The 5/8” steel stamp is heated for 60 seconds to reach 1550 ºF (843 ºC) and the desired hardness. Smaller parts will also heat easily.


Benefits:
  • Faster process time and production rates;
  • Hands-free heating that involves no operator skill for manufacturing;
  • Controlled precise application of heat.
Weniger
Weiterlesen

Senden Sie eine Anfrage

Interessieren Sie sich für dieses Produkt? Benötigen Sie zusätzliche Informationen oder individuelle Preise?

Kontaktiere uns
FRAGEN SIE NACH DEM PRODUKT close
Vielen Dank für die Zusendung Ihrer Nachricht. Wir werden so schnell wie möglich antworten.
FRAGEN SIE NACH DEM PRODUKT close
Durchsuche
Senden Sie eine Anfrage

Zur Wunschliste hinzufügen

Sie müssen eingeloggt sein

Hardening the end of steel hand-held marking stamps


Objective: To harden various size ends of hand held marking stamps. The area to be hardened is 3/4” (19mm) up the shank.


Equipment:
  • Ambrell 30 kW induction heating system, equipped with a remote workhead containing eight 1.0μF capacitors for a total of 2.0μF;
  • An induction heating coil designed and developed specifically for this application.

Material: Steel stamps 1/4” (6.3mm), 3/8” (9.5mm), 1/2” (12.7mm) and 5/8” (15.8mm) square


Temperature: 1550 ºF (843 ºC)



Frequency: 99 kHz


Process:

A two turn channel coil is used to cover the range of steel stamps being heated. The 5/8” steel stamp is heated for 60 seconds to reach 1550 ºF (843 ºC) and the desired hardness. Smaller parts will also heat easily.


Benefits:
  • Faster process time and production rates;
  • Hands-free heating that involves no operator skill for manufacturing;
  • Controlled precise application of heat.