U4720 + D72 two-component resin, polymerization at ambient temperature

Application:
Half hard system is used for electronic flooding.
- transformers,
- PCB,
- Electronic components flooding.

Description:
It is excellent resin with very good physical and electrical preferences. It is self - extinguished, and its compatible with insulation system class B.

Storage conditions:
We recommend:
- Storage away from light source, heat or cold, in the closed original container.
- PRODUCT HIGHLY SENSITIVE FOR HUMIDITY,
- storage time: 6 months in temperature
  10°C - 25°C.
For hardener: 12 months in temperature 5°C - 30°C,
- usage:open in ambient temperature

Hygiene and protection:
- Resin components don't corrode.
- it is prohibited to touch with skin, or inhale
- it is recommended to use gloves, glasses and mask.

Packing:
- in containers 1, 5 i 20 kg and barrels 220 kg,
- part B is delivered in corresponding proportion to part A.

 
Preliminary polymer part A Hardener part B
viscosity @ 30°C NSEG0013 25000 ± 6000 mPas viscosity @ 30°C NSEG0013 70 ± 20 mPas
Volume weight ISO 2811 1,61 g/ml Volume weight ISO 2811  
Colour   black Colour   brown
MIXTURE A + B
Mixture weight ratio   100/19 ± 1
Mixture volume ratio   79/21
Insert content   55 %
viscosity @ 23°C NSEG0013 6500 ± 1500 mPas
Volume weight ISO 2811 1,50 g/ml
lifetime NSEG0005 - min
Gelation time @ 23°C 150g NSEG0008 240 min
Gelation time @ 78°C NSEG0012 14 ± 0,4 min
Exothermic temperature 50g NSEG0007 27 °C
Exothermic temperature 100g NSEG0007 28 °C
Exothermic temperature 150g NSEG0007 29 °C
 
Polymerisation
W20°C NSEG0010 7h30min
W20°C NSEG0010 1h45min
Mechanical properties
Line shrinkage ISO3521  
Break off resistance ISO R 527 33,6 daN/cm2
Lengthening during break off ISO R 527 21,7%
Shore hardness A/D @ 23°CC ISO 868 80 A
Electrical properties
Dielectric withstand CEI 243 17kV/mm
Dielectric constant @ 23°C CEI 250 7 (50Hz)
Tgd przy 23°C CEI 250 8,53 x 10-3 (50Hz)
 
Thermal properties
Constant operation temperature   -50+125°C
Thermal conductance   W/m.°C
Glassy transformation   °C
Self - extinguished SEG V0 4mm

Send an inquiry

Are you interested in this product? Do you need additional information or individual pricing?

Contact us
ASK FOR THE PRODUCT close
Thank you for sending your message. We will respond as soon as possible.
ASK FOR THE PRODUCT close
Browse

Add to Wishlist

You must be logged in

Application:
Half hard system is used for electronic flooding.
- transformers,
- PCB,
- Electronic components flooding.

Description:
It is excellent resin with very good physical and electrical preferences. It is self - extinguished, and its compatible with insulation system class B.

Storage conditions:
We recommend:
- Storage away from light source, heat or cold, in the closed original container.
- PRODUCT HIGHLY SENSITIVE FOR HUMIDITY,
- storage time: 6 months in temperature
  10°C - 25°C.
For hardener: 12 months in temperature 5°C - 30°C,
- usage:open in ambient temperature

Hygiene and protection:
- Resin components don't corrode.
- it is prohibited to touch with skin, or inhale
- it is recommended to use gloves, glasses and mask.

Packing:
- in containers 1, 5 i 20 kg and barrels 220 kg,
- part B is delivered in corresponding proportion to part A.

 
Preliminary polymer part A Hardener part B
viscosity @ 30°C NSEG0013 25000 ± 6000 mPas viscosity @ 30°C NSEG0013 70 ± 20 mPas
Volume weight ISO 2811 1,61 g/ml Volume weight ISO 2811  
Colour   black Colour   brown
MIXTURE A + B
Mixture weight ratio   100/19 ± 1
Mixture volume ratio   79/21
Insert content   55 %
viscosity @ 23°C NSEG0013 6500 ± 1500 mPas
Volume weight ISO 2811 1,50 g/ml
lifetime NSEG0005 - min
Gelation time @ 23°C 150g NSEG0008 240 min
Gelation time @ 78°C NSEG0012 14 ± 0,4 min
Exothermic temperature 50g NSEG0007 27 °C
Exothermic temperature 100g NSEG0007 28 °C
Exothermic temperature 150g NSEG0007 29 °C
 
Polymerisation
W20°C NSEG0010 7h30min
W20°C NSEG0010 1h45min
Mechanical properties
Line shrinkage ISO3521  
Break off resistance ISO R 527 33,6 daN/cm2
Lengthening during break off ISO R 527 21,7%
Shore hardness A/D @ 23°CC ISO 868 80 A
Electrical properties
Dielectric withstand CEI 243 17kV/mm
Dielectric constant @ 23°C CEI 250 7 (50Hz)
Tgd przy 23°C CEI 250 8,53 x 10-3 (50Hz)
 
Thermal properties
Constant operation temperature   -50+125°C
Thermal conductance   W/m.°C
Glassy transformation   °C
Self - extinguished SEG V0 4mm