Keral 96

Keral 96

Alumina content 96%

Keral 96 is a base material for applying thick coats. This material has good electrical properties and good thermal conductivity. The other components are mainly SiO2, MgO and CaO. It is a low-cost alternative to a thick base material compared to Keral 99.

We laser cut the material according to your wishes!

Please submit your CAD data.

Typical features Unit Value
color - white
Gross density g/cm3 3,78
Surface Roughness Ra µm 0,6
Bending force MPa 400
Dielectric strength at 20°C kV/mm 15
Thermal expansion coefficient 20 - 600°C 10-6K-1 ~ 7
Thermal conductivity W/mK 24
Dimensions mm as desired
Thickness mm 0,25 do 1,5
Consistency - thick
Main ingredients % 96% Al2O3

Benefits

  • inexpensive base material
  • good electrical insulation properties
  • good mechanical strength
  • good thermal conductivity
  • the possibility of cutting with a laser or a wavy saw
  • good alignment

Usage

  • alumina substrate material for thick film technology
  • sensor protection plate
  • electrical insulator
Moins
Lire la suite

Envoyez une demande

Êtes-vous intéressé par ce produit? Avez-vous besoin d'informations supplémentaires ou d'une tarification individuelle?

Nous contacter
DEMANDEZ LE PRODUIT close
Merci d'avoir envoyé votre message. Nous vous répondrons dans les plus brefs délais.
DEMANDEZ LE PRODUIT close
Feuilleter
envoyer une demande

Ajouter à la liste de souhaits

Vous devez être connecté

Keral 96

Alumina content 96%

Keral 96 is a base material for applying thick coats. This material has good electrical properties and good thermal conductivity. The other components are mainly SiO2, MgO and CaO. It is a low-cost alternative to a thick base material compared to Keral 99.

We laser cut the material according to your wishes!

Please submit your CAD data.

Typical features Unit Value
color - white
Gross density g/cm3 3,78
Surface Roughness Ra µm 0,6
Bending force MPa 400
Dielectric strength at 20°C kV/mm 15
Thermal expansion coefficient 20 - 600°C 10-6K-1 ~ 7
Thermal conductivity W/mK 24
Dimensions mm as desired
Thickness mm 0,25 do 1,5
Consistency - thick
Main ingredients % 96% Al2O3

Benefits

  • inexpensive base material
  • good electrical insulation properties
  • good mechanical strength
  • good thermal conductivity
  • the possibility of cutting with a laser or a wavy saw
  • good alignment

Usage

  • alumina substrate material for thick film technology
  • sensor protection plate
  • electrical insulator