Epoksidinis - alkidinis modifikuotas lakas E521, E521T, E521ATX

Material is one component, for electrical insulation class F 155°C dry in drier.

Application:
- electro technical material class B and F,

Main preferences:
- impregnation lacquer made from modified alkyd - epoxide resin, great dielectric withstand and elastic preferences.
- it is resistant for humidity and transformer oils.
- it is compatible with cables in enamel class B, F and H,
- E521 T (tropical version) meets requirements 41514 NFX.

Material impregnation:
-By immersion, or vacuum. Its good stability allows to impregnate electrical devices, which are hot. However, it cannot be generalised to all motor types.
-lacquer hardens when polymerisation occurs without any oxidation. It is recommended to check if the diluent is removed when the drying begins.  

Polymerisation :
- preliminary component drying (40 4 50°C max.),
- immersion unit air blisters disappear
- drying depends on the weight of impregnated material.
- rise temperature up to 130°C,
- drying:
          class B: 4 hours in temp. 130 4 140°C,
          class F: 4 hours in temp. 150 4 160°C,
- Dry time can be changed according to the component weight,

Storage conditions:
12 months in original and closed package, far away from the sun and heat source

Packing:
-containers 1, 5 , 30 l or barrels 200 l.

Hygiene and protection:
Lacquer consists ksylen.

Lacquer Standard E521TE521AT E 521 ATX
Chemical origins   modified alkyd - epoxide modified alkyd - epoxide
Thermal class   (F)/155°C (F)/155°C
viscosity ISO 2431 40s +/-10s 40s+/-10s
density @ 20°C NFT30020 0,98 0,98
Ignition point - crucible closed NFT30020 26°C 26°C
Dry extract NSEG 0001 45% +/- 2 45% +/- 2
Colour   Orange Pomarańczowy
Drying on a plate NSEG 0002w150°C2 @ 150°C 2 h w 150°C45 min.
Diluent   37022 37022

Preferences:

Breakdown on a copper plate [thickness 0,01 mm] Volt
natural state 1400
After 8 days in humid air: 1250
After 8 days in destilated water: 1200
After 8 days in oil: 1430
mažiau
Skaityk daugiau

Atsiųskite užklausą

Ar Jūs domina šis produktas? Ar Jums reikia papildomos informacijos ar individualaus pasiūlymo?

Susisiekite su mumis
KLAUSKITE PRODUKTO close
Dėkojame, kad atsiuntėte žinutę. Atsakysime kuo greičiau.
KLAUSKITE PRODUKTO close
Naršyti
atsiųsti paklausimą

Pridėti į norų sąrašą

tu turi būti prisijungęs

Material is one component, for electrical insulation class F 155°C dry in drier.

Application:
- electro technical material class B and F,

Main preferences:
- impregnation lacquer made from modified alkyd - epoxide resin, great dielectric withstand and elastic preferences.
- it is resistant for humidity and transformer oils.
- it is compatible with cables in enamel class B, F and H,
- E521 T (tropical version) meets requirements 41514 NFX.

Material impregnation:
-By immersion, or vacuum. Its good stability allows to impregnate electrical devices, which are hot. However, it cannot be generalised to all motor types.
-lacquer hardens when polymerisation occurs without any oxidation. It is recommended to check if the diluent is removed when the drying begins.  

Polymerisation :
- preliminary component drying (40 4 50°C max.),
- immersion unit air blisters disappear
- drying depends on the weight of impregnated material.
- rise temperature up to 130°C,
- drying:
          class B: 4 hours in temp. 130 4 140°C,
          class F: 4 hours in temp. 150 4 160°C,
- Dry time can be changed according to the component weight,

Storage conditions:
12 months in original and closed package, far away from the sun and heat source

Packing:
-containers 1, 5 , 30 l or barrels 200 l.

Hygiene and protection:
Lacquer consists ksylen.

Lacquer Standard E521TE521AT E 521 ATX
Chemical origins   modified alkyd - epoxide modified alkyd - epoxide
Thermal class   (F)/155°C (F)/155°C
viscosity ISO 2431 40s +/-10s 40s+/-10s
density @ 20°C NFT30020 0,98 0,98
Ignition point - crucible closed NFT30020 26°C 26°C
Dry extract NSEG 0001 45% +/- 2 45% +/- 2
Colour   Orange Pomarańczowy
Drying on a plate NSEG 0002w150°C2 @ 150°C 2 h w 150°C45 min.
Diluent   37022 37022

Preferences:

Breakdown on a copper plate [thickness 0,01 mm] Volt
natural state 1400
After 8 days in humid air: 1250
After 8 days in destilated water: 1200
After 8 days in oil: 1430
mažiau
Skaityk daugiau
Komentarai (0)