F klasės Izoliacinės medžiagos
  • F klasės Izoliacinės medžiagos

Nuotraukos yra skirtos tik informaciniams tikslams. Peržiūrėkite produkto specifikaciją

please use latin characters

Gamintojas: SEG

F klasės Izoliacinės medžiagos

Marking:

Different  SEGPREG's have markings containing a letter and digit combination:

-1 :       T - thernomid NV,
-2 :       F - modified epoxide resin ,
-3 and 4:   divided by 100 indicates non pressed final product thickness
-5 and 6:   multiplied by 10 indicates weight for m2  of final product.

Characteristic:
Insulation material SEG type PF has better properties than normal insulation materials compatible with insulation class 155°C.

Polymerisation:
Temperature and polymerisation time can be adjusted to final product or resources: 3 min @190°C, 20 min @ 170°C, 45 min @150°C.

Storage:

SEGPREG's must be stored in cold room, far away from light and other heat sources, in temperature not higher than 25°C: 8 months with 5°C, 4 months with 23°C ± 2°C.

Preferences
Type Film thickness[mm] Surface weight Thickness non pressed Flow volatile parts weight
[mm]		 Break down voltage
[kV]
film
[g/m2]		 overall
[g/m2]		 resin
[g/m2]		 resin
[%]
Tolerance ±10% ±10% ±12% ±10% ±5% ±15% min.
TF 1718 0,15 142 180 35 19 0,17 < 0,8 < 1 8,3
TF 2121 0,18 177 215 38 19 0,21 < 0,8 < 1 9
TF 2425 0,2 212 255 45 20 0,24 < 0,8 < 1 9,6
TF 2729 0,24 247 290 43 18 0,27 < 0,8 < 1 10,5
TF 3338 0,3 338 385 45 14 0,33 < 0,8 < 1 11,6
Segpreg TFr - Initially impregnated insulation material (red)

Marking:
Different  SEGPREG's have markings containing a letter and digit combination:
-1:       T - THERNOMID NV,
-2:       F - modified epoxide resin
-3 and 4:   multiplied by 10 indicates non pressed final product thickness,
-5 and 6:   multiplied by 10 indicates weight for m2  of final product.

Characteristic:
It is well adjusted for insulation systems class 155°C.

Polymerisation:
Our recommendation: 3 min @ 190°C, 20 min @ 170°C, 45 min @ 150°C.

Storage:

SEGPREG's must be stored in cold room, far away from light and other heat sources, in temperature not higher than 25°C: 8 months with 5°C, 4 months with 23°C ± 2°C.

Preferences
  Unit Tolerance TFr2729 TFr3338 TFr3846 TFr4860
Film thickness mm ±15% 0,24 0,3 0,35 0,45
Film surface weight g/m2 ±12% 247 338 422 562
Overall surface weight g/m2 ±12% 290 385 465 600
Resin surface weight g/m2 ±10% 43 45 45 45
Resin layer % ±5 18 14 12 9
non pressed thickness mm ±15% 0,27 0,33 0,38 0,48
Flow %   < 0,8 < 0,8 < 0,8 < 0,8
violate parts %   < 1 < 1 < 1 < 1
break down voltage kV min. 10,6 11,6 14,6 18,6
THERNOMID 10.04 VF

Characteristic:
It is adjusted to insulation systems class F 155 °C.

Delivers:
Material can be delivered in rollers, sheets or groove insulation - for request.
Standard roller size: 1000mm.
Standard lengths on roller (thickness ± 0,5%):
0,05mm - 750m, 0,10mm - 380m, 0,15mm - 250m, 0,18mm - 210m, 0,24mm - 160m, 0,30mm - 120m, 0,40mm - 90m.

Preferences
  Thickness Tolerance 2.05 2.2 2.4 2.5 2.75 2.1 2.14
Thickness mm   0,05 0,1 0,15 0,18 0,24 0,3 0,4
Tolerance   ± % 15 15 15 15 15 10 10
Film thickness mm ±10% 12 50 100 125 190 250 350
Weight g/m2 ±12% 46 116 186 221 312 396 536
Efficiency m2/kg ±12% 21,7 8,6 5,4 4,5 3,2 2,5 1,9
Lengthening resistance MD N/cm min. 35 100 145 180 270 315 360
lengthening MD % min. 20 20 20 20 20 20 20
Stretching resistance TD N/cm min. 30 80 110 135 180 170 315
Stretch TD % min. 45 45 45 45 45 45 45
Break down voltage kV min. 2,5 4 6,5 7,5 12 15 19,5
 
THERNOMID20 04 VF
Characteristic:
-melting point: 255°C do 265°C,
-soften point: 245°C,
-thermal constant resistance: 155°C,
-thermal temporary resistance: 195°C,
-thermal withstand: -180°C in liquid nitrogen,
-shrink: 2% @. 160°C during 30 min,
-line expansion coefficient 3 x 10-5/°C,
-thermal conductance: 0,085 W/m°C,
-specific heat: 0,3 cal/g°C,
-water absorption: < 0,6% in water @25°C during 24h,
-break down voltage: see diagram
-resistance for stretching 180daN/cm2,
-stretch: 120%,
-Dielectric losses coefficient  @ 50 Hz (tδ)in temp. 20°C: 0, 005,
-dielectric constant 50 Hz (er) @ 20°C: 2, 45

THERNOMID20.04 VF is produced in 9 thicknesses

Thickness
[mm]		 Tolerance Polyester film thickness
[µ]		 substance
[g/m2]		 standard rollers
0,09 ± 10% 23 75 ± 10% 400 mb x 1000 mm
0,11 ± 10% 36 90 ± 10% 350 mb x 1000 mm
0,15 ± 5% 50 150 ± 10% 250 mb x 1000 mm
0,18 ± 5% 75 185 ± 10% 220 mb x 1000 mm
0,20 ± 5% 100 220 ± 1 10% 200 mb x 1000 mm
0,30 ± 5% 125 255 ± 10% 160 mb x 1000 mm
0,30 ± 5% 190 345 ± 10% 140 mb x 1000 mm
0,35 ± 5% 250 430 ± 10% 110 mb x 1000 mm
0,45 ± 5% 350 570 ± 10% 100 mb x 1000 mm

 

Break down voltage in thickness function
THERNOMID NV

Insulation material for system class F 155°C.

Characteristic:
-Dielectric withstand: 50 kV / mm,
dielectric constant 50 Hz @ 25°C: 2,46 przy 20°C,
-dielectric losses coefficient  @ 50 Hz 25°C: 0,005 przy 20°C,
-break down voltage: patrz wykres,
-melting point: > 250°C,
-soften point: > 245°C,
-thermal constant resistance: 155°C,
-thermal temporary resistance 190°C,
-thermal minimal withstand: - 180°C in liquid nitrogen,
-specific heat: 0,3 kal/g °C,
-thermal conductance: 0,085W/min°C,
-line stretch coefficient (30°C - 50°C): 3x10-5/°C,
-resistance for stretching 180 daN/cm2,
-stretch: 120%,
-shrink: 160°C @ 30min w 2%,
-absorption: < 0,6%.

THERNOMID NV is produced in 10 thicknesses

Thickness
[mm]		 Tolerance Polyester film thickness
[µ]		 substance
[g/m2]		 Standard rollers
0,09 ± 10% 23 69 ± 5% 400 mb x 1000 mm
0,10 ± 10% 36 87 ± 5% 350 mb x 1000 mm
0,15 ± 10% 50 142 ± 5% 250 mb x 1000 mm
0,18 ± 10% 75 177 ± 5% 220 mb x 1000 mm
0,20 ± 10% 100 212 ± 5% 200 mb x 1000 mm
0,23 ± 10% 75 215 ± 5% 160 mb x 1000 mm
0,24 ± 10% 125 247 ± 5% 160 mb x 1000 mm
0,30 ± 10% 190 338 ± 5% 140 mb x 1000 mm
0,35 ± 10% 250 422 ± 5% 110 mb x 1000 mm
0,45 ± 10% 350 562 ± 5% 100 mb x 1000 mm

Break down voltage in function of thickness
THERNOPHASE
Characteristic:
-melting point: 255°C do 265°C,
-soften point: 245°C,
-thermal constant resistance: 155°C,
-thermal temporary resistance: 180°C,
-shrink: 2% @temp. 160°C during 30 min,
-line expansion coefficient: 3x10-6/°C,
-break down voltage: 12 kV
-resistance for stretching: 120 daN/cm2,
-stretch: 120%.

THERNOPHASE is produced in 5 thicknesses

Thickness
[mm]

 Tolerance Polyester film thickness
[µ]		 substance
[g/m2]		 Standard rollers
0,33 ± 5% 50 150 ± 5% 200 mb x 1000 mm
0,36 ± 5% 75 185 ± 5% 160 mb x 1000 mm
0,38 ± 5% 100 220 ± 5% 140 mb x 1000 mm
0.40 ± 5% 125 255 ± 5% 120 mb x 1000 mm
0,47 ± 5% 190 340 ± 5% 100 mb x 1000 mm

break down voltage in function of thickness
SEGUIMEX TRIPLEX

Characteristic:
- melting point: 255°C do 265°C,
- soften point: 245°C,
- thermal constant resistance: 155°C,
- thermal temporary resistance: 190°C,
- thermal min withstand: -180°C in liquid nitrogen,
- shrink: 2% w temp. 160°C during 30 min.,
- line expansion coefficient: 3x10-5/°C,
- specific heat: 0,3 cal /g°C,
- absorption:: < 0,6% in water o temp. 25°C during24h,
- break down voltage: see chart on 1144 page,

 

Thickness
[mm]		 Tolerance Aramid paper thickness
[mm]		 Polyester film thickness
[µ]		 substance
[g/m2]		 Standard rollers
SEGUIMEX 5
0,15 ± 10% 0,05 36 140 ± 5% 250 mb x 914 mm
0,20 ± 10% 0,05 100 230 ± 5% 200 mb x 914 mm
0,25 ± 10% 0,05 125 265 ± 5% 160 mb x 914 mm
0,30 ± 10% 0,05 190 355 ± 5% 140 mb x 914 mm
0,35 ± 10% 0,05 250 440 ± 5% 110 mb x 914 mm
0,45 ± 10% 0,05 350 580 ± 5% 100 mb x 914 mm
 
SEGUIMEX 8
0,22 ± 10% 0,08 50 210 ± 5% 180 mb x 914 mm
0,25 ± 10% 0,08 75 245 ± 5% 150 mb x 914 mm
0,32 ± 10% 0,08 125 315 ± 5% 120 mb x 914 mm
0,40 ± 10% 0,08 250 405 ± 5% 100 mb x 914 mm
SEGUIMEX DUPLEX

 

Thickness
[mm]		 Tolerance Aramid paper thickness
[mm]		 Thickness błonki
poliestrowej
[µ]		 substance
[g/m2]		 Standard rollers
SEGUIMEX 5
0,23 ± 10% 0,05 175 294 ± 5% 160 mb x 914 mm
0,30 ± 10% 0,05 250 399 ± 5% 120 mb x 914 mm
 
SEGUIMEX 8
0,19 ± 10% 0,08 100 213 ± 5% 200 mb x 914 mm
0,26 ± 10% 0,08 175 319 ± 5% 160 mb x 914 mm
0,33 ± 10% 0,08 250 424 ± 5% 120 mb x 914 mm
0,43 ± 10% 0,08 350 563 ± 5% 100 mb x 914 mm

 

break down voltage in function of thickness

THERNOSTRAT20.04 VF

 

Characteristic:
-dielectric withstand: NFC 26225 52 kV/mm,
-break down voltage: NFC26230 patrz krzywa kV,
-melting point: Fischer-Jones >250 °C,
-soften point: ASTM D 876-65 >245 °C,
-constant operation temperature: NFC26205 155 °C,
-max temporary temperature: NFC26205 190°C,
-min operating temperature: NFC26205 -180 °C w ciekłym azocie,
-specific heat: NF PRG 62011 i ASTM C 518 0,3 cal/g °C,
-line expansion coefficient(z 30 do 50°C): ASTM D 696-44 0,00003 mm/°C,
-shrink @ 160°C during 30 min:   < 1,5%,
-zdolność do wchłaniania wody: NSEG 0017 < 0,6 %.

THERNOSTRAT 20.04 VF is produced in 8 thicknesses

Thickness - Tolerance Weight
[g/m2]		 Standard size
1,0 ± 10% 1174 ± 10% 980 mm x 980 mm
1,5 ± 10% 1766 ± 10% 980 mm x 980 mm
2,0 ± 10% 2350 ± 10% 980 mm x 980 mm
2,5 ± 10% 3050 ± 10% 980 mm x 980 mm
3,0 ± 10% 3672 ± 10% 980 mm x 980 mm
4,0 ± 10% 4895 ± 10% 980 mm x 980 mm
4,5 ± 10% 5870 ± 10% 980 mm x 980 mm
5,0 ± 10% 6457 ± 10% 980 mm x 980 mm

 

break down voltage in function of thickness
mažiau
Skaityk daugiau

Atsiųskite užklausą

Ar Jūs domina šis produktas? Ar Jums reikia papildomos informacijos ar individualaus pasiūlymo?

Susisiekite su mumis
KLAUSKITE PRODUKTO close
Dėkojame, kad atsiuntėte žinutę. Atsakysime kuo greičiau.
KLAUSKITE PRODUKTO close
Naršyti
atsiųsti paklausimą

Pridėti į norų sąrašą

tu turi būti prisijungęs

Marking:

Different  SEGPREG's have markings containing a letter and digit combination:

-1 :       T - thernomid NV,
-2 :       F - modified epoxide resin ,
-3 and 4:   divided by 100 indicates non pressed final product thickness
-5 and 6:   multiplied by 10 indicates weight for m2  of final product.

Characteristic:
Insulation material SEG type PF has better properties than normal insulation materials compatible with insulation class 155°C.

Polymerisation:
Temperature and polymerisation time can be adjusted to final product or resources: 3 min @190°C, 20 min @ 170°C, 45 min @150°C.

Storage:

SEGPREG's must be stored in cold room, far away from light and other heat sources, in temperature not higher than 25°C: 8 months with 5°C, 4 months with 23°C ± 2°C.

Preferences
Type Film thickness[mm] Surface weight Thickness non pressed Flow volatile parts weight
[mm]		 Break down voltage
[kV]
film
[g/m2]		 overall
[g/m2]		 resin
[g/m2]		 resin
[%]
Tolerance ±10% ±10% ±12% ±10% ±5% ±15% min.
TF 1718 0,15 142 180 35 19 0,17 < 0,8 < 1 8,3
TF 2121 0,18 177 215 38 19 0,21 < 0,8 < 1 9
TF 2425 0,2 212 255 45 20 0,24 < 0,8 < 1 9,6
TF 2729 0,24 247 290 43 18 0,27 < 0,8 < 1 10,5
TF 3338 0,3 338 385 45 14 0,33 < 0,8 < 1 11,6
Segpreg TFr - Initially impregnated insulation material (red)

Marking:
Different  SEGPREG's have markings containing a letter and digit combination:
-1:       T - THERNOMID NV,
-2:       F - modified epoxide resin
-3 and 4:   multiplied by 10 indicates non pressed final product thickness,
-5 and 6:   multiplied by 10 indicates weight for m2  of final product.

Characteristic:
It is well adjusted for insulation systems class 155°C.

Polymerisation:
Our recommendation: 3 min @ 190°C, 20 min @ 170°C, 45 min @ 150°C.

Storage:

SEGPREG's must be stored in cold room, far away from light and other heat sources, in temperature not higher than 25°C: 8 months with 5°C, 4 months with 23°C ± 2°C.

Preferences
  Unit Tolerance TFr2729 TFr3338 TFr3846 TFr4860
Film thickness mm ±15% 0,24 0,3 0,35 0,45
Film surface weight g/m2 ±12% 247 338 422 562
Overall surface weight g/m2 ±12% 290 385 465 600
Resin surface weight g/m2 ±10% 43 45 45 45
Resin layer % ±5 18 14 12 9
non pressed thickness mm ±15% 0,27 0,33 0,38 0,48
Flow %   < 0,8 < 0,8 < 0,8 < 0,8
violate parts %   < 1 < 1 < 1 < 1
break down voltage kV min. 10,6 11,6 14,6 18,6
THERNOMID 10.04 VF

Characteristic:
It is adjusted to insulation systems class F 155 °C.

Delivers:
Material can be delivered in rollers, sheets or groove insulation - for request.
Standard roller size: 1000mm.
Standard lengths on roller (thickness ± 0,5%):
0,05mm - 750m, 0,10mm - 380m, 0,15mm - 250m, 0,18mm - 210m, 0,24mm - 160m, 0,30mm - 120m, 0,40mm - 90m.

Preferences
  Thickness Tolerance 2.05 2.2 2.4 2.5 2.75 2.1 2.14
Thickness mm   0,05 0,1 0,15 0,18 0,24 0,3 0,4
Tolerance   ± % 15 15 15 15 15 10 10
Film thickness mm ±10% 12 50 100 125 190 250 350
Weight g/m2 ±12% 46 116 186 221 312 396 536
Efficiency m2/kg ±12% 21,7 8,6 5,4 4,5 3,2 2,5 1,9
Lengthening resistance MD N/cm min. 35 100 145 180 270 315 360
lengthening MD % min. 20 20 20 20 20 20 20
Stretching resistance TD N/cm min. 30 80 110 135 180 170 315
Stretch TD % min. 45 45 45 45 45 45 45
Break down voltage kV min. 2,5 4 6,5 7,5 12 15 19,5
 
THERNOMID20 04 VF
Characteristic:
-melting point: 255°C do 265°C,
-soften point: 245°C,
-thermal constant resistance: 155°C,
-thermal temporary resistance: 195°C,
-thermal withstand: -180°C in liquid nitrogen,
-shrink: 2% @. 160°C during 30 min,
-line expansion coefficient 3 x 10-5/°C,
-thermal conductance: 0,085 W/m°C,
-specific heat: 0,3 cal/g°C,
-water absorption: < 0,6% in water @25°C during 24h,
-break down voltage: see diagram
-resistance for stretching 180daN/cm2,
-stretch: 120%,
-Dielectric losses coefficient  @ 50 Hz (tδ)in temp. 20°C: 0, 005,
-dielectric constant 50 Hz (er) @ 20°C: 2, 45

THERNOMID20.04 VF is produced in 9 thicknesses

Thickness
[mm]		 Tolerance Polyester film thickness
[µ]		 substance
[g/m2]		 standard rollers
0,09 ± 10% 23 75 ± 10% 400 mb x 1000 mm
0,11 ± 10% 36 90 ± 10% 350 mb x 1000 mm
0,15 ± 5% 50 150 ± 10% 250 mb x 1000 mm
0,18 ± 5% 75 185 ± 10% 220 mb x 1000 mm
0,20 ± 5% 100 220 ± 1 10% 200 mb x 1000 mm
0,30 ± 5% 125 255 ± 10% 160 mb x 1000 mm
0,30 ± 5% 190 345 ± 10% 140 mb x 1000 mm
0,35 ± 5% 250 430 ± 10% 110 mb x 1000 mm
0,45 ± 5% 350 570 ± 10% 100 mb x 1000 mm

 

Break down voltage in thickness function
THERNOMID NV

Insulation material for system class F 155°C.

Characteristic:
-Dielectric withstand: 50 kV / mm,
dielectric constant 50 Hz @ 25°C: 2,46 przy 20°C,
-dielectric losses coefficient  @ 50 Hz 25°C: 0,005 przy 20°C,
-break down voltage: patrz wykres,
-melting point: > 250°C,
-soften point: > 245°C,
-thermal constant resistance: 155°C,
-thermal temporary resistance 190°C,
-thermal minimal withstand: - 180°C in liquid nitrogen,
-specific heat: 0,3 kal/g °C,
-thermal conductance: 0,085W/min°C,
-line stretch coefficient (30°C - 50°C): 3x10-5/°C,
-resistance for stretching 180 daN/cm2,
-stretch: 120%,
-shrink: 160°C @ 30min w 2%,
-absorption: < 0,6%.

THERNOMID NV is produced in 10 thicknesses

Thickness
[mm]		 Tolerance Polyester film thickness
[µ]		 substance
[g/m2]		 Standard rollers
0,09 ± 10% 23 69 ± 5% 400 mb x 1000 mm
0,10 ± 10% 36 87 ± 5% 350 mb x 1000 mm
0,15 ± 10% 50 142 ± 5% 250 mb x 1000 mm
0,18 ± 10% 75 177 ± 5% 220 mb x 1000 mm
0,20 ± 10% 100 212 ± 5% 200 mb x 1000 mm
0,23 ± 10% 75 215 ± 5% 160 mb x 1000 mm
0,24 ± 10% 125 247 ± 5% 160 mb x 1000 mm
0,30 ± 10% 190 338 ± 5% 140 mb x 1000 mm
0,35 ± 10% 250 422 ± 5% 110 mb x 1000 mm
0,45 ± 10% 350 562 ± 5% 100 mb x 1000 mm

Break down voltage in function of thickness
THERNOPHASE
Characteristic:
-melting point: 255°C do 265°C,
-soften point: 245°C,
-thermal constant resistance: 155°C,
-thermal temporary resistance: 180°C,
-shrink: 2% @temp. 160°C during 30 min,
-line expansion coefficient: 3x10-6/°C,
-break down voltage: 12 kV
-resistance for stretching: 120 daN/cm2,
-stretch: 120%.

THERNOPHASE is produced in 5 thicknesses

Thickness
[mm]

 Tolerance Polyester film thickness
[µ]		 substance
[g/m2]		 Standard rollers
0,33 ± 5% 50 150 ± 5% 200 mb x 1000 mm
0,36 ± 5% 75 185 ± 5% 160 mb x 1000 mm
0,38 ± 5% 100 220 ± 5% 140 mb x 1000 mm
0.40 ± 5% 125 255 ± 5% 120 mb x 1000 mm
0,47 ± 5% 190 340 ± 5% 100 mb x 1000 mm

break down voltage in function of thickness
SEGUIMEX TRIPLEX

Characteristic:
- melting point: 255°C do 265°C,
- soften point: 245°C,
- thermal constant resistance: 155°C,
- thermal temporary resistance: 190°C,
- thermal min withstand: -180°C in liquid nitrogen,
- shrink: 2% w temp. 160°C during 30 min.,
- line expansion coefficient: 3x10-5/°C,
- specific heat: 0,3 cal /g°C,
- absorption:: < 0,6% in water o temp. 25°C during24h,
- break down voltage: see chart on 1144 page,

 

Thickness
[mm]		 Tolerance Aramid paper thickness
[mm]		 Polyester film thickness
[µ]		 substance
[g/m2]		 Standard rollers
SEGUIMEX 5
0,15 ± 10% 0,05 36 140 ± 5% 250 mb x 914 mm
0,20 ± 10% 0,05 100 230 ± 5% 200 mb x 914 mm
0,25 ± 10% 0,05 125 265 ± 5% 160 mb x 914 mm
0,30 ± 10% 0,05 190 355 ± 5% 140 mb x 914 mm
0,35 ± 10% 0,05 250 440 ± 5% 110 mb x 914 mm
0,45 ± 10% 0,05 350 580 ± 5% 100 mb x 914 mm
 
SEGUIMEX 8
0,22 ± 10% 0,08 50 210 ± 5% 180 mb x 914 mm
0,25 ± 10% 0,08 75 245 ± 5% 150 mb x 914 mm
0,32 ± 10% 0,08 125 315 ± 5% 120 mb x 914 mm
0,40 ± 10% 0,08 250 405 ± 5% 100 mb x 914 mm
SEGUIMEX DUPLEX

 

Thickness
[mm]		 Tolerance Aramid paper thickness
[mm]		 Thickness błonki
poliestrowej
[µ]		 substance
[g/m2]		 Standard rollers
SEGUIMEX 5
0,23 ± 10% 0,05 175 294 ± 5% 160 mb x 914 mm
0,30 ± 10% 0,05 250 399 ± 5% 120 mb x 914 mm
 
SEGUIMEX 8
0,19 ± 10% 0,08 100 213 ± 5% 200 mb x 914 mm
0,26 ± 10% 0,08 175 319 ± 5% 160 mb x 914 mm
0,33 ± 10% 0,08 250 424 ± 5% 120 mb x 914 mm
0,43 ± 10% 0,08 350 563 ± 5% 100 mb x 914 mm

 

break down voltage in function of thickness

THERNOSTRAT20.04 VF

 

Characteristic:
-dielectric withstand: NFC 26225 52 kV/mm,
-break down voltage: NFC26230 patrz krzywa kV,
-melting point: Fischer-Jones >250 °C,
-soften point: ASTM D 876-65 >245 °C,
-constant operation temperature: NFC26205 155 °C,
-max temporary temperature: NFC26205 190°C,
-min operating temperature: NFC26205 -180 °C w ciekłym azocie,
-specific heat: NF PRG 62011 i ASTM C 518 0,3 cal/g °C,
-line expansion coefficient(z 30 do 50°C): ASTM D 696-44 0,00003 mm/°C,
-shrink @ 160°C during 30 min:   < 1,5%,
-zdolność do wchłaniania wody: NSEG 0017 < 0,6 %.

THERNOSTRAT 20.04 VF is produced in 8 thicknesses

Thickness - Tolerance Weight
[g/m2]		 Standard size
1,0 ± 10% 1174 ± 10% 980 mm x 980 mm
1,5 ± 10% 1766 ± 10% 980 mm x 980 mm
2,0 ± 10% 2350 ± 10% 980 mm x 980 mm
2,5 ± 10% 3050 ± 10% 980 mm x 980 mm
3,0 ± 10% 3672 ± 10% 980 mm x 980 mm
4,0 ± 10% 4895 ± 10% 980 mm x 980 mm
4,5 ± 10% 5870 ± 10% 980 mm x 980 mm
5,0 ± 10% 6457 ± 10% 980 mm x 980 mm

 

break down voltage in function of thickness
mažiau
Skaityk daugiau