Alumina content 96%
Keral 96 is a base material for applying thick coats. This material has good electrical properties and good thermal conductivity. The other components are mainly SiO2, MgO and CaO. It is a low-cost alternative to a thick base material compared to Keral 99.
We laser cut the material according to your wishes!
Please submit your CAD data.
Typical features | Unit | Value |
---|---|---|
color | - | white |
Gross density | g/cm3 | 3,78 |
Surface Roughness Ra | µm | 0,6 |
Bending force | MPa | 400 |
Dielectric strength at 20°C | kV/mm | 15 |
Thermal expansion coefficient 20 - 600°C | 10-6K-1 | ~ 7 |
Thermal conductivity | W/mK | 24 |
Dimensions | mm | as desired |
Thickness | mm | 0,25 do 1,5 |
Consistency | - | thick |
Main ingredients | % | 96% Al2O3 |
Benefits
Usage
Sunteți interesat de acest produs? Aveți nevoie de informații suplimentare sau de prețuri individuale?
trebuie să fii logat
Alumina content 96%
Keral 96 is a base material for applying thick coats. This material has good electrical properties and good thermal conductivity. The other components are mainly SiO2, MgO and CaO. It is a low-cost alternative to a thick base material compared to Keral 99.
We laser cut the material according to your wishes!
Please submit your CAD data.
Typical features | Unit | Value |
---|---|---|
color | - | white |
Gross density | g/cm3 | 3,78 |
Surface Roughness Ra | µm | 0,6 |
Bending force | MPa | 400 |
Dielectric strength at 20°C | kV/mm | 15 |
Thermal expansion coefficient 20 - 600°C | 10-6K-1 | ~ 7 |
Thermal conductivity | W/mK | 24 |
Dimensions | mm | as desired |
Thickness | mm | 0,25 do 1,5 |
Consistency | - | thick |
Main ingredients | % | 96% Al2O3 |
Benefits
Usage
Aprecierea ta pentru recenzie nu a putut fi trimisa
Reclama un comentariu
Raport trimis
Reclamatia tau nu a putut fi trimisa
Scrie-ti recenzia
Recenzia a fost trimisa
Recenzia ta nu a putut fi trimisa