Application:
Half hard resin is used to flooding in electronic and electro technical industry.
- transformers
- PCB
- electronic components flooding
General characteristic:
It is great resin with good electric and physics properties.
It is self - extinguished, has good thermal conductance and it's compatible with class B insulation system.
Storage conditions
It is recommended to: :
- Storage far away from light, cold or heat. In original, closed container. Product is very sensitive for humidity
Packing:
1-5 -12 and 20 kg containers or barrels 220 kg
part B is delivered in corresponding proportion to part A..
Life time: 12 months in temperature 10°C i 25°C A and for hardener 12 months in temperature 5°C i 30°C.
Usage: Open in ambient temperature 48h before usage.
Protection and hygiene:
- Resin components don't corrode.
- it is prohibited to touch with skin, or inhale
- it is recommended to use gloves, glasses and mask.
Characteristic | ||||||||
---|---|---|---|---|---|---|---|---|
Preliminary polymer part A | Hardener part B | |||||||
viscosity @ 23°C | NSEG 0013 | 10 000 | mPas | viscosity @ 23°C | NSEG 0013 | 70 | mPas | |
(Reomat) | +/- 3 000 | (Reomat) | +/- 50 | mPas | ||||
Weight | ISO 2811 | 1.72 | g/ml | Weight | ISO 2811 | 1.17 | g/ml | |
Colour | Black |
|
Brown |
MIXTURE | |||||||
---|---|---|---|---|---|---|---|
Physical | Mechanical | ||||||
Mixture weight ratio |
100/ 16 | +/- 1 | Line shrinkage | ISO 3521 | < 0.5 | % | |
Mixture volume ratio | 81 / 19 | Break off resistance | ISO R 527 | 25 | daN/cm2 | ||
Insert content | 56 | % | Lengthening during break off | ISO R 527 | 19 | % | |
viscosity @ 23°C | NSEG 0013 | 4 000 | mPas | Shore hardness A/D @ 23°C | ISO 868 | 70 | A |
(Reomat) | +/- 1 200 | ||||||
Volume weight | ISO 2811 | 1.65 | g/ml | Dielectrical | |||
lifetime 150 g @ 23°C | NSEG 0005 | 11 | min. | Stiffness | CEI 243 | 21 | KV/mm |
Gelation time @ 23°C - 150 g | NSEG 0008 | 25 | min. | Constant @ 23°C | CEI 250 | 3.12 | (50 Hz) |
Gelation time @ 78°C - 2.5 g | NSEG 0012 | 3'40'' | min. | Tg d a 23°C | CEI 250 | 17.7 10-3 | (50 Hz) |
+/- 70'' | Through resistance | Ohm.cm | |||||
Exothermic peak - 50 g | NSEG 0007 | 29 | °C | Thermal properties | |||
Exothermic peak - 100 g | NSEG 0007 | 31 | °C | Constant operation temperature | - 50 +125 | °C | |
Exothermic peak - 200 g | NSEG 0007 | 31 | °C | For constant usage | |||
Thermal conductance | 0.488 | W/m.°C | |||||
Polymerisation or drying | Glassy transformation | °C | |||||
@ 20°C | NSEG 0010 | 4 H | 30 mn | Flammability | SEG | V0 | 5.5 mm |
@ 60°C | NSEG 0010 | 1 H | 15 mn |
Да ли вас занима овај производ? Да ли су вам потребне додатне информације или појединачне цене?
морате бити пријављени
Application:
Half hard resin is used to flooding in electronic and electro technical industry.
- transformers
- PCB
- electronic components flooding
General characteristic:
It is great resin with good electric and physics properties.
It is self - extinguished, has good thermal conductance and it's compatible with class B insulation system.
Storage conditions
It is recommended to: :
- Storage far away from light, cold or heat. In original, closed container. Product is very sensitive for humidity
Packing:
1-5 -12 and 20 kg containers or barrels 220 kg
part B is delivered in corresponding proportion to part A..
Life time: 12 months in temperature 10°C i 25°C A and for hardener 12 months in temperature 5°C i 30°C.
Usage: Open in ambient temperature 48h before usage.
Protection and hygiene:
- Resin components don't corrode.
- it is prohibited to touch with skin, or inhale
- it is recommended to use gloves, glasses and mask.
Characteristic | ||||||||
---|---|---|---|---|---|---|---|---|
Preliminary polymer part A | Hardener part B | |||||||
viscosity @ 23°C | NSEG 0013 | 10 000 | mPas | viscosity @ 23°C | NSEG 0013 | 70 | mPas | |
(Reomat) | +/- 3 000 | (Reomat) | +/- 50 | mPas | ||||
Weight | ISO 2811 | 1.72 | g/ml | Weight | ISO 2811 | 1.17 | g/ml | |
Colour | Black |
|
Brown |
MIXTURE | |||||||
---|---|---|---|---|---|---|---|
Physical | Mechanical | ||||||
Mixture weight ratio |
100/ 16 | +/- 1 | Line shrinkage | ISO 3521 | < 0.5 | % | |
Mixture volume ratio | 81 / 19 | Break off resistance | ISO R 527 | 25 | daN/cm2 | ||
Insert content | 56 | % | Lengthening during break off | ISO R 527 | 19 | % | |
viscosity @ 23°C | NSEG 0013 | 4 000 | mPas | Shore hardness A/D @ 23°C | ISO 868 | 70 | A |
(Reomat) | +/- 1 200 | ||||||
Volume weight | ISO 2811 | 1.65 | g/ml | Dielectrical | |||
lifetime 150 g @ 23°C | NSEG 0005 | 11 | min. | Stiffness | CEI 243 | 21 | KV/mm |
Gelation time @ 23°C - 150 g | NSEG 0008 | 25 | min. | Constant @ 23°C | CEI 250 | 3.12 | (50 Hz) |
Gelation time @ 78°C - 2.5 g | NSEG 0012 | 3'40'' | min. | Tg d a 23°C | CEI 250 | 17.7 10-3 | (50 Hz) |
+/- 70'' | Through resistance | Ohm.cm | |||||
Exothermic peak - 50 g | NSEG 0007 | 29 | °C | Thermal properties | |||
Exothermic peak - 100 g | NSEG 0007 | 31 | °C | Constant operation temperature | - 50 +125 | °C | |
Exothermic peak - 200 g | NSEG 0007 | 31 | °C | For constant usage | |||
Thermal conductance | 0.488 | W/m.°C | |||||
Polymerisation or drying | Glassy transformation | °C | |||||
@ 20°C | NSEG 0010 | 4 H | 30 mn | Flammability | SEG | V0 | 5.5 mm |
@ 60°C | NSEG 0010 | 1 H | 15 mn |
Vaša zahvalnost na komentar ne može biti registrovana
Prijavite nepristojan komentar
Prija nepristojnog komentara registrovana
Vaša prijava nepristojnog komentara ne može biti registrovana
Napišite vaš komentar
Komentar poslat
Vaš komentar ne može biti registrovan