Keral 96
  • Keral 96

Фотографії призначені тільки для інформаційних цілей. Подивитися специфікацію продукту

please use latin characters

Виробник: Kerafol

Keral 96

Keral 96

Alumina content 96%

Keral 96 is a base material for applying thick coats. This material has good electrical properties and good thermal conductivity. The other components are mainly SiO2, MgO and CaO. It is a low-cost alternative to a thick base material compared to Keral 99.

We laser cut the material according to your wishes!

Please submit your CAD data.

Typical features Unit Value
color - white
Gross density g/cm3 3,78
Surface Roughness Ra µm 0,6
Bending force MPa 400
Dielectric strength at 20°C kV/mm 15
Thermal expansion coefficient 20 - 600°C 10-6K-1 ~ 7
Thermal conductivity W/mK 24
Dimensions mm as desired
Thickness mm 0,25 do 1,5
Consistency - thick
Main ingredients % 96% Al2O3

Benefits

  • inexpensive base material
  • good electrical insulation properties
  • good mechanical strength
  • good thermal conductivity
  • the possibility of cutting with a laser or a wavy saw
  • good alignment

Usage

  • alumina substrate material for thick film technology
  • sensor protection plate
  • electrical insulator
Менше
Читати більше

Відправити запит

Ви зацікавлені у цьому продукті? Вам потрібна додаткова інформація або індивідуальні розцінки?

Зв'яжіться з нами
Запитайте про продукт close
Дякуємо за надіслане повідомлення. Ми відповімо якомога швидше.
Запитайте про продукт close
Огляд
Надіслати запит

Додати до списку бажань

Ви повинні увійти в систему

Keral 96

Alumina content 96%

Keral 96 is a base material for applying thick coats. This material has good electrical properties and good thermal conductivity. The other components are mainly SiO2, MgO and CaO. It is a low-cost alternative to a thick base material compared to Keral 99.

We laser cut the material according to your wishes!

Please submit your CAD data.

Typical features Unit Value
color - white
Gross density g/cm3 3,78
Surface Roughness Ra µm 0,6
Bending force MPa 400
Dielectric strength at 20°C kV/mm 15
Thermal expansion coefficient 20 - 600°C 10-6K-1 ~ 7
Thermal conductivity W/mK 24
Dimensions mm as desired
Thickness mm 0,25 do 1,5
Consistency - thick
Main ingredients % 96% Al2O3

Benefits

  • inexpensive base material
  • good electrical insulation properties
  • good mechanical strength
  • good thermal conductivity
  • the possibility of cutting with a laser or a wavy saw
  • good alignment

Usage

  • alumina substrate material for thick film technology
  • sensor protection plate
  • electrical insulator