Application
Half stiff polyurethane systems are recommended for closed electronic and electro technical systems used in industry:
- in transformers,
- for electric component flooding,
- for PCB flooding.
Main characteristic:
It is self - extinguished, has good thermal conductance, has compatibility with insulation system class B. acji klasy B.
Storage conditions:
It is recommended to:
- Storage far away from light, heat, cold source, in original closed container.
- product highly sensitive for humidity,
- storage time: 4 months in temperature 10°C - 25°C,
- hardener: 12 months in temperature 5°C - 30°C,
- usage: bring to ambient temperature 48 hours before usage.
Packing:
- in containers 1, 5 i 20 kg and barrels 220 kg,
- part B is delivered in corresponding proportion to part A..
Preliminary polymer part A | Hardener part B | ||||
---|---|---|---|---|---|
viscosity @ 23°C | NSEG0013 | 3200 ± 50 mPas | viscosity @ 23°C | NSEG0013 | 000 ± 50 mPas |
Volume weight | ISO 2811 | 1,45 g/ml | Volume weight | ISO 2811 | 1,23 g/ml |
Colour | black | Volume weight | brown |
Mixture A + B | ||
---|---|---|
Mixture weight ratio | 100/16 ± 1 | |
Mixture volume ratio | - | |
Insert content | -% | |
viscosity @ 23°C | NSEG0013 | 4000 ± 1200 mPas |
Volume weight | ISO 2811 | 1.40 g/ml |
lifetime 150 g @ 23°C | NSEG 0005 | 10 min |
Gelation time @ 23°C | 45 do 60 min | |
Gelation time @ 50°C | 25 do 30 min | |
Exothermic peak @ 50 g | NSEG 0007 | - °C |
Exothermic peak @ 100 g | NSEG 0007 | - °C |
Exothermic peak @ 5 kg | NSEG 0007 | 42°C |
Polymerization | ||
W20°C | NSEG 0010 | 8 h. 30 min |
W60°C | NSEG 0010 | 2 h. 30 min |
Mechanical properties | ||
Line shrinkage | ISO 3521 | < 0,5 % |
Break off resistance | ISO R 527 | 2 |
Lengthening during break off | ISO R 527 | <19% |
Shore hardness A/D @ 23°C | ISO 868 | 85 A |
Electrical properties | ||
Dielectric withstand | CEI 243 | >15kV/mm |
Dielectric constant @ 23°C | CEI 250 | 4,2 (50Hz) |
Loss coefficient @ 23°C | CEI 250 | 0.04 (50Hz) |
Resistivity | 3*1013 | Ω/cm |
Thermal properties | ||
Constant operation temperature | od-30°Cdo130°C | |
Thermal conductance | 0,65 W/m.°C | |
Self - extinguished | UL 94 | V0 6mm |
Ви зацікавлені у цьому продукті? Вам потрібна додаткова інформація або індивідуальні розцінки?
Ви повинні увійти в систему
Application
Half stiff polyurethane systems are recommended for closed electronic and electro technical systems used in industry:
- in transformers,
- for electric component flooding,
- for PCB flooding.
Main characteristic:
It is self - extinguished, has good thermal conductance, has compatibility with insulation system class B. acji klasy B.
Storage conditions:
It is recommended to:
- Storage far away from light, heat, cold source, in original closed container.
- product highly sensitive for humidity,
- storage time: 4 months in temperature 10°C - 25°C,
- hardener: 12 months in temperature 5°C - 30°C,
- usage: bring to ambient temperature 48 hours before usage.
Packing:
- in containers 1, 5 i 20 kg and barrels 220 kg,
- part B is delivered in corresponding proportion to part A..
Preliminary polymer part A | Hardener part B | ||||
---|---|---|---|---|---|
viscosity @ 23°C | NSEG0013 | 3200 ± 50 mPas | viscosity @ 23°C | NSEG0013 | 000 ± 50 mPas |
Volume weight | ISO 2811 | 1,45 g/ml | Volume weight | ISO 2811 | 1,23 g/ml |
Colour | black | Volume weight | brown |
Mixture A + B | ||
---|---|---|
Mixture weight ratio | 100/16 ± 1 | |
Mixture volume ratio | - | |
Insert content | -% | |
viscosity @ 23°C | NSEG0013 | 4000 ± 1200 mPas |
Volume weight | ISO 2811 | 1.40 g/ml |
lifetime 150 g @ 23°C | NSEG 0005 | 10 min |
Gelation time @ 23°C | 45 do 60 min | |
Gelation time @ 50°C | 25 do 30 min | |
Exothermic peak @ 50 g | NSEG 0007 | - °C |
Exothermic peak @ 100 g | NSEG 0007 | - °C |
Exothermic peak @ 5 kg | NSEG 0007 | 42°C |
Polymerization | ||
W20°C | NSEG 0010 | 8 h. 30 min |
W60°C | NSEG 0010 | 2 h. 30 min |
Mechanical properties | ||
Line shrinkage | ISO 3521 | < 0,5 % |
Break off resistance | ISO R 527 | 2 |
Lengthening during break off | ISO R 527 | <19% |
Shore hardness A/D @ 23°C | ISO 868 | 85 A |
Electrical properties | ||
Dielectric withstand | CEI 243 | >15kV/mm |
Dielectric constant @ 23°C | CEI 250 | 4,2 (50Hz) |
Loss coefficient @ 23°C | CEI 250 | 0.04 (50Hz) |
Resistivity | 3*1013 | Ω/cm |
Thermal properties | ||
Constant operation temperature | od-30°Cdo130°C | |
Thermal conductance | 0,65 W/m.°C | |
Self - extinguished | UL 94 | V0 6mm |